Polypropylene/Basalt fabric laminates: Flexural properties and impact damage behavior

Recently, the growing interests into the environmental matter are driving the research interest to the development of new eco-sustainable composite materials toward the replacement of synthetic reinforcing fibers with natural ones and exploiting the intrinsic recyclability of thermoplastic resins even for uses in which thermosetting matrices are well consolidated (e.g., naval and aeronautical fields). In this work, polypropylene/basalt fabric composite samples were prepared by film stacking and compression molding procedures. They have been studied in terms of flexural and low-velocity impact behavior. The influence related to the matrix modification with a pre-optimized amount of maleic anhydride grafted PP as coupling agent was studied. The mechanical performances of the composite systems were compared with those of laminates consisting of the pure matrix and obtained by hot-pressing of PP pellets and PP films used in the stacking procedure. Results, on one side, demonstrated a slight reduction of both static and dynamic parameters at the break for specimens from superimposed films to ones prepared from PP pellets. Moreover, an outstanding improvement of mechanical performances was shown in the presence of basalt layers, especially for compatibilized samples.