Ultra-high-temperature ceramic matrix composites (UHTCMCs) based on a ZrB2/SiC matrix have been investigated for the fabrication of reusable nozzles for propulsion. Three de Laval nozzle prototypes, obtained by sintering with either hot pressing (HP) or spark plasma sintering (SPS), were tested 2–3 times in a hybrid rocket motor for proving reusability. Sections were extracted after oxidation tests to study the microstructural changes and oxidative and thermomechanical stresses induced by the repeated tests. Compared to a reference graphite nozzle, no measurable erosion was observed for the UHTCMC-based nozzles. The oxidation mechanism consisted in the formation of a ZrO2 intermediate layer, with a liquid silicon oxide (SiO2) layer on the surface that was displaced by the action of the gas flux towards the divergent part of the nozzle, protecting it from further oxidation. Both specimens obtained by HP and SPS displayed similar performance, with very slight differences, which were attr...
Propulsion tests on ultra-high-temperature ceramic matrix composites for reusable rocket nozzles / Sciti, Diletta; Vinci, Antonio; Zoli, Luca; Galizia, Pietro; Failla, Simone; Mungiguerra, Stefano; Di Martino, Giuseppe D.; Cecere, Anselmo; Savino, Raffaele. - In: JOURNAL OF ADVANCED CERAMICS. - ISSN 2226-4108. - 12:(2023), pp. 1-1360. [10.26599/JAC.2023.9220759]
Propulsion tests on ultra-high-temperature ceramic matrix composites for reusable rocket nozzles
Mungiguerra, Stefano;Di Martino, Giuseppe D.;Cecere, Anselmo;Savino, Raffaele
2023
Abstract
Ultra-high-temperature ceramic matrix composites (UHTCMCs) based on a ZrB2/SiC matrix have been investigated for the fabrication of reusable nozzles for propulsion. Three de Laval nozzle prototypes, obtained by sintering with either hot pressing (HP) or spark plasma sintering (SPS), were tested 2–3 times in a hybrid rocket motor for proving reusability. Sections were extracted after oxidation tests to study the microstructural changes and oxidative and thermomechanical stresses induced by the repeated tests. Compared to a reference graphite nozzle, no measurable erosion was observed for the UHTCMC-based nozzles. The oxidation mechanism consisted in the formation of a ZrO2 intermediate layer, with a liquid silicon oxide (SiO2) layer on the surface that was displaced by the action of the gas flux towards the divergent part of the nozzle, protecting it from further oxidation. Both specimens obtained by HP and SPS displayed similar performance, with very slight differences, which were attr...I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.