Wood powders of different botanical origin as an alternative to barrel aging for red wine

Wood powders are produced in large quantity as by-product of barrel, staves and chips industry. Differently from larger particles (chips), the use of wood powders in winemaking is not admitted (Regulation (CE) n. 934/2019); however, it could represent a cheap and sustainable alternative for the accelerated aging of red wine. To evaluate their potential use in winemaking, a comparative study on the use of wood powders from oak, chestnut and acacia wood for the accelerated aging of red wine (cv. Aglianico) was conducted. This alternative aging was compared to the aging in wood barrels from the same botanical species. The wine aged in contact with powders underwent a quicker evolution of polyphenolic fraction. After 15 days of contact, the loss of total anthocyanins was higher than that observed after 6 months of aging in barrels (from 4 to 14% with respect to the corresponding kind of barrel). The amount of polymeric pigments tannins–anthocyanins–tannins in wines aged in contact with powders was higher respect to the wines aged in barrels (from 7 to 21% with respect to the corresponding kind of barrel), while the greatest loss of total tannins was detected in the oak barrels (28% less with respect to the control). There were several differences in wine phenolic acids due to wood botanical origin, with the clearest differences being between oak and the alternative wood species (chestnut and acacia). Also, there was a significant botanical effect on sensory profiles. Indeed, both among barrels and among powders, oak wood was the one that gave the strongest wood odor character. However, all the treatments with wood powders (oak, acacia and chestnut) preserved the fruity character of wine, conferring in the meanwhile non-dominant woody notes.